Study of Performance of Hybrid yarns (Hemp/ Polypropylene/ Glass) Woven Reinforcements

N/A
N/A
Protected

Academic year: 2017

Share "Study of Performance of Hybrid yarns (Hemp/ Polypropylene/ Glass) Woven Reinforcements "

Copied!
5
0
0

Texto

Loading

Imagem

Fig. 2 Reinforcements elastic modulus, MPa  The  elastic  modulus  (Fig.2)  is  2.3  times  higher  with
Table 3 Composites Surface Parameters and Physical - Mechanical Properties  Designation  Composite thickness,  mm  Surface  density, g/m2 Tensile  strength,  N  Tensile  extension,  %  Tensile stress, MPa  Elastic  modulus, MPa  C_I  0.34  311  303.1  0.61

Referências

Documentos relacionados

The present investigation was performed to study the influence of the fiber content on the strain rate depend- ency of Young’s modulus, tensile strength and failure mechanisms of

he objective of this study was to process and characterize multifunctional composites, based on epoxy resin/glass iber (GF) woven fabric prepreg and CF/Ni veil, a non-woven material,

Alguns instrumentos multidimensionais de avaliação do risco de quedas para pessoas idosas que vivem na comunidade, como o Falls Risk for Older People in the Community (FROP-com)

Considerando a relevância do tema em questão e com a finalidade de contribuir com as ações de prevenção e controle das infecções hospitalares desenvolvidas pelo SCIH do

Abstract: The objective of this study was to compare the lexural strength and elasticity modulus of two types of staple reinforcement i- bers, Interlig - Ângelus 

As ligações químicas ocorrem pela interação dos elétrons mais externos com os átomos vizinhos em busca da estabilidade:.. o Recebendo ou doando um ou

ABSTRACT - The objective of this study was to evaluate the efficiency of using nylon textiles (50 µ m), F57 (Ankom ® ) and non-woven textile (NWT - 100 g/m 2 ) on

Among this study’s limitations, it is possible to conclude that for external hexagon implant, the higher elastic modulus of the ceramic crowns associated with lower elastic modulus