eISSN 2280-8000 ORIGINAL RESEARCH ARTICLEacid copolymer (7). Setting reactions begin immediately after mixing powder which contains glass particles with acid liquid.
The fluoro-alumino-silicate glasses are degraded after the acid attack, releasing calcium and aluminum ions, which are che- lated by the carboxylate groups and crosslink the polyalkenoic acid chains (6). This crosslinking process contains complex re- actions and continues for some weeks after initial hardening, leading to increased mechanical properties of GICs.
With the aim of overcoming the disadvantages of the ini- tial stage of GIC setting, it has been recommended to acceler- ate the maturation process, providing external energy (8-10).
Two methods have been used for this purpose: the applica- tion of ultrasonic waves, and the application of radiant heat from a dental light-curing unit. Regarding these methods, previous studies reported improved early mechanical proper- ties (11, 12), enhanced resistance to water degradation and better adaptation to cavity walls (13).
After mixing of a glass ionomer material and as the setting reaction continues, the hardness of the material increases and achieves the highest values when the reaction completes (14). Moreover, fluoride release is very high in the beginning of the GIC setting and drops as the maturation of the mate- rial proceeds (15). As a matter of fact, the surface hardness and fluoride release of a GIC may indicate the stage of its maturation.
DOI: 10.5301/jabfm.5000292
Effect of radiant heat and ultrasound on fluoride
release and surface hardness of glass ionomer cements
Kosmas Tolidis, Dimitrios Dionysopoulos, Paris Gerasimou, Thrasyvoulos Sfeikos
Department of Operative Dentistry, School of Dentistry, Aristotle University of Thessaloniki, Thessaloniki - Greece
Introduction
Glass ionomer cements (GICs) are broadly used for dental restorations in daily clinical practice (1) due to their advan- tageous properties such as fluoride release, which provides anticariogenic activity (2), good biocompatibility (3), and chemical bond to the dental tissues (4). However, they are sensitive to moisture and have slow maturing reactions, re- sulting in delays in the development of the final strength of the materials (5), which may be achieved 3 months after mix- ing of the cement (6).
GICs are formed by a neutralization reaction between typi- cal fluoro-alumino-silicate glasses and aqueous solution of polyalkenoic acids, such as polyacrylic acid or acrylic/maleic
AbSTRACT
Purpose: The purpose of this investigation was to evaluate the influence of radiant heat and ultrasound on fluo- ride release and surface hardness of 3 glass ionomer cements (GICs).
Methods: There were 3 experimental groups for each GIC; in group 1, the specimens were left to set without any treatment; in group 2, the specimens were irradiated for 2 minutes using a LED unit; and in group 3, ultrasound was applied using a scaler for 55 seconds on the specimen surface. Fluoride release measurements were per- formed daily for 7 days and at days 14 and 28. Surface hardness of the tested GICs was determined using Vickers method. The measurements were performed 24 hours and 7 days after mixing. Statistical analysis of the data was made using 1-way ANOVA and Tukey’s and Bonferroni post hoc tests (α = 0.05).
Results: Radiant heat during setting reduced the fluoride release and increased the surface hardness of GICs (p<0.05). Ultrasonic treatment also reduced the fluoride release and increased the surface hardness (p<0.05) of GICs but in lower extent. Among the GICs there were differences in fluoride release and surface hardness proper- ties depending on their composition (p<0.05).
Conclusions: Radiant heat and ultrasonic treatments may be useful methods for GIC restorations in order to achieve faster adequate initial mechanical properties.
Keywords: Fluoride release, Glass ionomers, Microhardness, Radiant heat, Ultrasound
Accepted: March 19, 2016 Published online: June 3, 2016 Corresponding author:
Dr. Dimitrios Dionysopoulos Department of Operative Dentistry School of Dentistry
Aristotle University of Thessaloniki 54124, Thessaloniki, Greece ddiondent@gmail.com
Author
personal
copy
Thus, the aim of this in vitro study was to evaluate the influence of radiant heat and ultrasound on fluoride release and surface hardness of 3 conventional GICs and how their composition affects these properties. The following 3 null hypotheses (Ho) were set in the current study. Ho1 stated that fluoride release and surface hardness of the tested GICs are not affected by application of radiant heat during setting. Ho2 stated that fluoride release and surface hard- ness of the tested GICs are not influenced by application of ultrasound during setting. Ho3 stated that the tested GICs present the same fluoride release and surface hardness properties.
Materials and methods Materials
Three contemporary conventional GICs were investigat- ed (Ketac Fil Plus Aplicap – KF, Ketac Universal Aplicap – KU, Equia Fil – EF). The tested glass ionomer materials were sup- plied in capsulated form and the shade was A3.5. Their tech- nical characteristics are shown in Table I.
Experimental groups of the study
Thirty cylindrical specimens of each GIC were prepared.
The dimensions of the specimens were 7 mm in diameter and 2 mm in thickness and were prepared using Teflon molds, re- sulting in 90 specimens in total. There were 3 experimental groups (n = 10) for each glass ionomer material. In group 1 (control group), after preparation the specimens were left in the mold to set without any treatment. In group 2 the top surface of the specimens was irradiated for 2 minutes us- ing an LED unit (Elipar S10; 3M ESPE) at 1,200 mW/cm2 with standard curing mode. The highest temperature recorded at the tip of the LED unit during 2 minutes of irradiation was 54.7oC. The diameter of the light tip of the device was 9 mm and there was no distance between the light tip and the top surface of the specimen during irradiation. In group 3, ultra- sound was applied on the top surface of the specimens using an ultrasonic hand piece with a flat tip scaler (2 mm wide) of Suprasson P5 Newtron (Satelec, Acteon Group). The param- eters for the handpiece device were 36 KHz frequency with the maximum power setting, without water spray. The flat
tip was moved continuously for 55 seconds on the specimen surface in a uniform manner over a polyester strip with a light hand pressure.
Preparation of specimens
The mixing of the glass ionomer materials for the prepa- ration of the specimens performed according to manufactur- ers’ instructions in room temperature (23 ± 1oC). The capsule was activated and immediately transferred to a rotating mixer (RotoMixTM; 3M ESPE) for mixing for recommended time. Sub- sequently, the capsule was loaded into the gun and the cement was immediately injected into the mold. Prior to placing the material into the mold, a polyester strip was placed on a glass slab; the mold was then placed and the GIC packed. After plac- ing the GIC, a second polyester strip was placed on top of the mold and a glass microscope slide was placed over the GIC in order to achieve a standardized surface finishing and to remove the excess of the material. The glass ionomer specimens were left to set in the mold for the appropriate time of each mate- rial (7 minutes for KF and KU and 5 minutes for EF from the beginning of the mixing) and then they were removed care- fully. Subsequently, the prepared specimens were immersed individually and suspended with nonfluoride dental floss in 4 mm of deionized water in a plastic container at 37 ± 1oC.
Fluoride ion release measurements
First, the fluoride ion release measurement was per- formed for each specimen 24 hours after mixing. One milliliter of deionized water was rinsed on each specimen above the plastic container and then the specimens were transferred to a new plastic container with fresh 4 mL of deionized water.
Subsequently, 0.5 mL of total ionic strength adjustment buf- fer (TISAB III; Thermo Fisher Scientific) was added into the solution. The fluoride ion concentration was then evaluated using a fluoride ion-selective electrode (Orion 9609BNWP, Ionplus Sure-Flow Fluoride; Thermo Scientific) coupled to a bench top analyzer (Orion StarTM Series ISE Meter; Thermo Scientific) with a detection limit at ± 0.01 ppm. All measure- ments were carried out at room temperature (23 ± 1oC) and data were converted to μg/cm2F- units. Fluoride concentra- tion analysis was continued for all experimental groups daily for 7 days and then for days 14 and 28.
TAbLE I - The technical characteristics of the tested materials
Material Category Manufacturer Composition
Ketac Fil Plus Aplicap Conventional GIC (capsules) 3M ESPE Powder: Sodium-strontium-aluminum-lanthanum- fluoro-phospho-silicate glass and pigments
Liquid: Water, copolymer of acrylic acid-maleic acid, tartaric acid
Ketac Universal Aplicap Conventional GIC (capsules) 3M ESPE Powder: Oxide glass
Liquid: Water, copolymer of acrylic acid-maleic acid, tartaric acid
Equia Fil Conventional GIC (capsules) GC Dental Powder: Fluoro-alumino-silicate glass70-80%
Liquid: Polyacrylic acid 10-15% Distilled water 10-15%
Author
personal
copy
Measurement of surface hardness
Eighteen specimens of each GIC were prepared using the same method as described previously for fluoride release assessment. In addition, the experimental groups (n = 6) were the same as mentioned above. Surface hardness was determined by Vickers method using a microhardness tester (HMV-2000; Shimadzu) at a load of 200 g with an indenta- tion time of 10 seconds. The measurements were performed 24 hours and 7 days after specimen preparation. During the experimental period the specimens were immersed in 4 mm of deionized water individually and the solution was renewed daily. Five indentations were made on top surfaces of each GIC specimen, 1 in the center of the surface and 1 in every quadrant. The dimensions of the indentations were evalu- ated using the optical microscope of the hardness tester and the data were independently averaged and reported in Vick- ers Hardness Numbers (VHN).
Statistical analysis
Statistical analysis of the data was done by SPSS 20.0 and performed using 1-way ANOVA. The differences in fluoride concentrations among the experimental groups were de- tected using Bonferroni post hoc test (a = 0.05). Paired t-test and nonparametric Wilcoxon test were done in order to com- pare the cumulative fluoride release among the experimental groups (a = 0.05). One-way ANOVA and Tukey’s post-hoc test were used to compare the mean surface hardness between the GICs for each experimental group (a = 0.05).
Results
Fluoride release data
Fluoride release patterns (μg/cm2) of the treatment groups separately for each tested GIC during the 28-day pe- riod are presented in Figure 1 A-C. Figure 2 A-C illustrates the fluoride release patterns (μg/cm2) of the GICs, separately for each treatment group during the 28-day period.
Mean values and standard deviations of cumulative fluo- ride release expressed in μg/cm2 F- during the 28-day period of the GICs for all the experimental groups are presented in Table II. In all treatment groups, EF specimens released the greatest amounts of fluoride ions (almost double for irradi- ant heat and ultrasound groups) among the GICs (p<0.05).
Cumulative fluoride release of KF and KU did not differ sig- nificantly in control and radiant heat groups (p>0.05), while in ultrasound groups KF specimens released significantly larger amounts of fluoride compared to those of KU (p<0.05).
Statistical analysis revealed significant differences in cumulative fluoride release among the treatment groups (p<0.05). In particular, control groups of the GICs exhibited the highest cumulative fluoride release (p<0.05) during the experimental period followed by ultrasound groups, except for EF which did not present significant difference (p = 0.11).
The lowest cumulative fluoride release was obtained from ra- diant heat groups in all tested GICs (p<0.05). The reduction of cumulative fluoride release in comparison with control groups was in ultrasound groups: 42.6% for KU, 36.5% for KF
and 6.6% for EF; in radiant heat groups: 53.1% for KF, 50.0%
for KU and 25.0% for EF.
Surface hardness data
Mean values and standard deviations of surface hardness (VHN) of the experimental groups of the study 24 hours and 7 days after the preparation of the specimens are presented in Table III. After 24 hours, the surface hardness among GICs was significantly different, regardless of the treatment of the specimens during setting. More specifically, EF exhibited the highest surface hardness in control and ultrasound groups Fig. 1 - Fluoride release patterns (μg/cm2) of the treatment groups during the 28-day period: (A) Ketac Fill Aplicap; (b) Ketac Universal Aplicap; (C) Equia Fill.
Author
personal
copy
followed by KU and KF (p<0.05). However, in radiant heat groups KU presented significantly higher surface hardness than EF (p<0.05).
Among the treatment groups, the highest surface hard- ness was observed in specimen groups irradiated with the LED unit, followed by those that received ultrasonic treat- ment, while the control groups presented the lowest values (p<0.05). Exceptions were observed only for EF between radi- ant heat and ultrasound groups and for KF between control and ultrasound groups, for which the differences in surface hardness were not statistically significant (p>0.05).
The increase in surface hardness (% of the control group values) after treatments of the GICs during setting is also shown in Table III. The increase ranged for radiant heat groups between 32.7% and 71.7% and for ultrasound groups between 12.7% and 48.4%. The highest increase in surface hardness presented KU (71.7% in the radiant heat group).
After 7 days, the surface hardness of the GICs increased in all experimental groups. In control groups the rise of surface hardness ranged from 15.9% to 57%, in radiant heat groups from 10% to 35.4%, and in ultrasound groups from 11.7% to 26%.
Discussion
The outcomes obtained from the current study demand the rejection of Ho1 which states that fluoride release and surface hardness of the tested GICs are not affected by the application of radiant heat during setting. This is in agree- ment with previous investigations, which evaluated the effect of radiant heat on fluoride release (15) and surface hardness (8, 14, 16) of GICs.
In the current study all the GICs presented lower fluoride release after radiant heat treatment compared to control groups. This phenomenon may be due to the acceleration of the initial setting of GICs by the effects of heat from the den- tal LED unit, which may reduce the burst effect of the first process of fluoride release taking place in the first hours after mixing.
It is important to mention that induced heat – and not the light output – of the light-curing unit is crucial for the ac- celeration of the setting (10). Consequently, the parameters of a light source that are related to the effectiveness of this method are its thermal emission and the duration of the ir- radiation. In the present study, the specimens were irradiat- ed for an extended time (2 minutes) in order to deliver more thermal energy to the GICs.
Fig. 2 - Fluoride release patterns (μg/cm2) of the tested GICs during the 28-day period: (A) control groups; (b) radiant heat groups; (C) ultrasound groups.
TAbLE II - Cumulative fluoride release (μg/cm2) during days 1-28
Glass ionomers Control Radiant heat % reduction Ultrasound % reduction
Ketac Fil Plus Aplicap 386.14 (35.32)Aa 181.29 (17.39)Ab 53.1% 245.29 (20.42)Ac 36.5%
Ketac Universal Aplicap 360.10 (29.65)Aa 179.88 (21.02)Ab 50.0% 206.71 (21.27)Bc 42.6%
Equia Fil 492.08 (46.76)Ba 369.00 (33.66)Bb 25.0% 459.71 (41.04)Ca 6.6%
Mean values and standard deviations (SD) of surface hardness (VHN) of the experimental groups of the study after 24 hours and 7 days. The increase of surface hardness (% of the control groups) after treatments is also presented. The percentages in italics below the values indicate the increase of hardness after 7 days.
Same uppercase superscripts in columns indicate no statistically significant difference between materials (p>0.05). Same lowercase superscripts in rows indicate no statistically significant difference between treatments (p>0.05).
Author
personal
copy
After radiant heat treatment the fluoride release of the GICs decreased. This phenomenon may influence the an- ticariogenic properties of GICs. Dijkman and Arends (17) demonstrated that cumulative fluoride ion release of 200 to 300 μg/cm2 during a month is adequate to completely in- hibit enamel demineralization. In the current study the radi- ant heat groups of KF and KU released 181.29 ± 17.39 and 179.88 ± 21.02 μg/cm2 F- during the 28-day period.
The nature of the setting reaction in GICs results in an improvement of surface hardness with time (14). This coin- cides with the outcomes of the current study, which revealed an increase in surface hardness in all experimental groups 24 hours and 7 days after mixing. However, the increase in surface hardness was highest in radiant heat groups after 7 days compared to control groups. The outcomes of the cur- rent study are in agreement with those of previous studies (8, 14, 16). In contrast, a recent study (18) reported no effect of heat application on Vickers hardness of 3 conventional GICs.
The increase in surface hardness may be explained by heat transfer from the LED unit to GIC, leading to increased ion mobility at the first stage of setting. Heat transfer reduces the viscosity of the material and leads to the acceleration of the setting reactions (14).
Statistical analysis revealed that Ho2 is rejected. This states that fluoride release and surface hardness of the test- ed GICs are not influenced by the application of ultrasound during the setting. This result is in agreement with previous studies regarding fluoride release (19, 20) and surface hard- ness (14, 16).
In the current investigation, cumulative fluoride release of the tested GICs decreased after application of ultrasound.
Ultrasonic treatment provides heat transfer to the GIC speci- mens, which as mentioned above leads to the acceleration of the initial stage of the setting and as a consequence to the reduction of fluoride release. Consequently, a decrease in anticariogenic properties of the glass ionomer materials may
be observed. In contrast, Thanjal et al (19), who focused on the kinetics of fluoride ion release from GICs after ultrasound and radiant heat treatments concluded that ultrasound ap- plication increases fluoride release from GICs. In addition, they found that heat reduces fluoride release. The authors assumed that induced heat by ultrasonic treatment is not its only effect and agreed with Rushe and Towler (20) who sug- gested the most likely explanation is the enhanced reaction due to greater glass surface area available for reaction. Al- though heat induced by ultrasonic treatment is not the only effect on GIC surface, the outcomes of the present study in- dicate that the heat effect seems to dominate compared to the other effects.
Various suggestions have been made regarding the ways that ultrasonic waves may improve the properties of GICs when applied during setting (8, 21). More specifically, add- ing kinetic energy from the ultrasonic treatment to the GIC increases the rate of the reaction because of the temperature rise. Kleverlaan et al (8) observed a temperature increase around 13oC for GIC specimens treated with ultrasonic scaler.
However, O’Brien et al (14) did not find a significant tem- perature increase between glass ionomer specimens treated with ultrasonic scaler in comparison with control group speci- mens. As a result the authors concluded that an enhanced setting rate of GICs after ultrasonic treatment is less affected by temperature rise and more by mechanical excitation of the scaler tip itself.
It has been postulated that motivation of the scaler en- hances the glass particle mixing with polyalkenoic acid chains, resulting in homogenous reaction kinetics. Ultrasonic treat- ment may have a declustering effect on the glass particles, leading to a larger reactive surface area and thus to a reduced time of GIC setting (8, 22). Previous studies reported that high-frequency vibration of the GICs due to the motivation of the scaler tip enhances the mixing of glass ionomer compo- nents, resulting in a reduction in volume and number of voids TAbLE III - Surface hardness
Surface hardness (VHN) after 24 hours
Materials Control Radiant heat %VHN increase Ultrasound %VHN increase
Ketac Fil Plus Aplicap 9.28 (1.96)Aa 22.87 (3.04)Ab 59.4% 10.63 (1.31)Aa 12.7%
Ketac Universal Aplicap 15.90 (2.12)Ba 56.15 (4.39)Bb 71.7% 30.83 (3.17)Bc 48.4%
Equia Fil 28.54 (2.86)Ca 42.40 (3.69)Cb 32.7% 39.92 (3.11)Cb 28.5%
Surface hardness (VHN) after 7 days
Materials Control Radiant heat %VHN increase Ultrasound %VHN increase
Ketac Fil Plus Aplicap 11.03 (1.88)Aa 35.40 (3.00)Ab 68.8% 14.37 (1.42)Ac 23.2%
15.9% 35.4% 26.0%
Ketac Universal Aplicap 36.94 (3.10)Ba 81.60 (5.35)Bb 54.7% 37.51 (3.51)Ba 1.5%
57.0% 31.2% 17.8%
Equia Fil 39.91 (2.96)Ba 47.13 (3.29)Cb 15.3% 45.22 (3.88)Cb 11.7%
28.5% 10.0% 11.7%
Mean values and standard deviations (SD) of cumulative fluoride release (μg/cm2) from the tested glass ionomer materials during the 28-day experimental period. The % reduction of cumulative fluoride release after treatments in comparison with control groups is also presented. Same uppercase superscripts in columns indicate no statistically significant difference between materials (p>0.05). Same lowercase superscripts in rows indicate no statistically significant dif- ference between treatments (p>0.05).
Author
personal
copy
present in the material (23, 24). In addition, the increased temperature of the scaler tip during ultrasonic treatment may cause evaporation of the liquid of the GIC, increasing the powder/liquid ratio and, consequently, leading to higher me- chanical properties (8).
In the present study, the surface hardness of the GICs in- vestigated increased after ultrasonic treatment but to a lower extent compared to radiant heat treatment. This may be at- tributed to differences in the duration of the 2 treatments.
This phenomenon is related to the acceleration of the setting process due to the ultrasonic energy that was provided, as de- scribed earlier. Previous investigations confirm this evidence (8, 14, 24, 25) and reported a reduction of the setting time of GICs ranging from 45 seconds to 3 minutes after ultrasonic treatment (13, 24, 26). In contrast, Daifalla and Mobarak (27) reported that ultrasound treatment on 3 high viscous GICs for 20 or 40 seconds did not enhance the surface microhardness of the materials.
According to the results of the current study, Ho3 is reject- ed. This states that the tested GICs present the same fluoride release and surface hardness properties. Fluoride release contains complex reactions and can be influenced by several intrinsic and experimental factors, such as type of glass par- ticles and polyalkenoic acid, inherent fluoride content, solu- bility and porosity of the material, powder/liquid ratio used in preparing the material, method of mixing, and type of stor- age media (28, 29). Some of these factors may be the reason that the tested GICs exhibited different fluoride release abili- ties in this study. EF released the largest amounts of fluoride ions during the experiment among the materials investigated.
However, after 2 days the level of fluoride release is very close to the other 2 GICs regardless of the treatment during setting.
As a result, EF may not have better anticariogenic activities compared to the others (30).
Surface hardness of the tested GICs increased significantly 24 hours and 7 days after mixing. Differences among the ma- terials in surface hardness may be explained by differences in composition. More specifically, the integrity of the interface between the glass particles and the matrix may improve the setting reaction and as a result the mechanical properties of GICs. Furthermore, different sizes and shapes of glass par- ticles dispersed in the matrix enable a more efficient packing and consequently a higher integrated glass particle-polyacid matrix, leading to increased hardness of the material (14, 25).
It has been found that powder/liquid ratios and molecular weight, viscosity and concentration of polyalkenoic acid af- fect the properties of GICs (29, 31).
Conclusions
Within the limitation of this in vitro study, it can be con- cluded that irradiation for 2 minutes with a dental LED unit reduces fluoride release and increases surface hardness of the tested GICs. Furthermore, application of an ultrasonic scaler tip for 55 seconds on the surface of the tested GICs also reduces fluoride release and increases surface hardness of the materials, but to a lower extent. These discrepancies may be mainly attributed to differences in treatment durations.
Among the tested GICs there are differences in fluoride re- lease; surface hardness properties may be due to differences
in their composition. Radiant heat and ultrasonic treatments may be useful methods for GIC restorations in order to faster achieve adequate initial mechanical properties, which is cru- cial for the longevity of the dental restorations. Nevertheless, a disadvantage of these methods is the reduction of fluoride release from the glass ionomer materials.
Disclosures
Financial support: No grants or funding have been received for this study.
Conflict of interest: None of the authors has financial interest re- lated to this study to disclose.
References
1. Luponio C, Causa F, Angelini E, Pinasco MR, Ambrosio L. Effect of micrometer-scale metallic fillers on the mechanical and cor- rosion resistance properties of alternative materials for conser- vative dentistry. J Appl Biomater Biomech. 2006;4(3):143-152.
2. Dionysopoulos D. The effect of fluoride-releasing restorative materials on inhibition of secondary caries formation. Fluo- ride. 2014;47(3):258-265.
3. Rodriguez IA, Ferrara CA, Campos-Sanchez F, Alaminos M, Echevarría JU, Campos A. An in vitro biocompatibility study of conventional and resin-modified glass ionomer cements. J Ad- hes Dent. 2013;15(6):541-546.
4. Smith DC. Polyacrylic acid-based cements: adhesion to enamel and dentin. Oper Dent. 1992;(Suppl 5):177-183.
5. de Gee AJ, van Duinen RN, Werner A, Davidson CL. Early and long-term wear of conventional and resin-modified glass iono- mers. J Dent Res. 1996;75(8):1613-1619.
6. Matsuya S, Maeda T, Ohta M. IR and NMR analyses of hard- ening and maturation of glass-ionomer cement. J Dent Res.
1996;75(12):1920-1927.
7. Nicholson JW. Chemistry of glass-ionomer cements: a review.
Biomaterials. 1998;19(6):485-494.
8. Kleverlaan CJ, van Duinen RNB, Feilzer AJ. Mechanical prop- erties of glass ionomer cements affected by curing methods.
Dent Mater. 2004;20(1):45-50.
9. Talal A, Tanner KE, Billington R, Pearson GJ. Effect of ultrasound on the setting characteristics of glass ionomer cements studied by Fourier transform infrared spectroscopy. J Mater Sci Mater Med. 2009;20(1):405-411.
10. Gavic L, Gorseta K, Glavina D, Czarnecka B, Nicholson JW. Heat transfer properties and thermal cure of glass-ionomer dental cements. J Mater Sci Mater Med. 2015;26(10):249.
11. Gorseta K, Glavina D, Skrinjaric I. Influence of ultrasonic excita- tion and heat application on the microleakage of glass ionomer cements. Aust Dent J. 2012;57(4):453-457.
12. Barata TJE, Bresciani E, Adachi A, Fagundes TC, Carvalho CAR, Navarro MFL. Influence of ultrasonic setting on compressive and diametral tensile strengths of glass ionomer cements.
Mater Res. 2008;11(1):57-61.
13. Twomey E, Towler MR, Crowley CM, Doyle J, Hampshire S.
Investigation into the ultrasonic setting of glass ionomer ce- ments, Part II Setting times and compressive strengths. J Mater Sci. 2004;39(14):4631-4632.
14. O’Brien T, Shoja-Assadi F, Lea SC, Burke FJT, Palin WM. Extrinsic energy sources affect hardness through depth during set of a glass-ionomer cement. J Dent. 2010;38(6):490-495.
15. Dionysopoulos D, Koliniotou-Koumpia E, Kotsanos N. The effect of low-concentration fluoride solutions on fluoride recharge ability of contemporary dental restoratives and adhesives. Fluo- ride. 2015;48(4):351-363.
Author
personal
copy
16. Dehurtevent M, Deveaux E, Hornez JC, Robberecht L, Tabary N, Chai F. Influence of heat and ultrasonic treatments on the setting and maturation of a glass-ionomer cement.
Am J Dent. 2015;28(2):105-110.
17. Dijkman GE, Arends J. Secondary caries in situ around fluoride- releasing light-curing composites: a quantitative model investi- gation on four materials with a fluoride content between 0 and 26 vol%. Caries Res. 1992;26(5):351-357.
18. Menne-Happ U, Ilie N. Effect of heat application on the me- chanical behaviour of glass ionomer cements. Clin Oral Inves- tig. 2014;18(2):643-650.
19. Thanjal NK, Billington RW, Shahid S, Luo J, Hill RG, Pearson GJ.
Kinetics of fluoride ion release from dental restorative glass ion- omer cements: the influence of ultrasound, radiant heat and glass composition. J Mater Sci Mater Med. 2010;21(2):589-595.
20. Rushe N, Towler MR. The influence of ultrasonic setting on fluoride release from glass polyalkenoate cements. J Mater Sci.
2006;41(17):5775-5777.
21. Azevedo ER, Coldebella CR, Zuanon ACC. Effect of ultrasonic excitation on the microtensile bond strength of glass ionomer cements to dentin after different water storage times. Ultra- sound Med Biol. 2011;37(12):2133-2138.
22. Towler MR, Crowley CM, Hill RG. Investigation into the ultra- sonic setting of glass ionomer cements. Part I: Postulated mo- dalities. J Mater Sci Lett. 2003;22(7):539-541.
23. Coldebella CR, Santos-Pinto L, Zuanon ACC. Effect of ultra- sonic excitation on the porosity of glass ionomer cement: a scanning electron microscope evaluation. Microsc Res Tech.
2011;74(1):54-57.
24. Towler MR, Bushby AJ, Billington RW, Hill RG. A preliminary comparison of the mechanical properties of chemically cured
and ultrasonically cured glass ionomer cements, using nano- indentation techniques. Biomaterials. 2001;22(11):1401-1406.
25. Carvalho CA, Fagundes TC, Barata TJ, Navarro MFL. Influence of ultrasonic setting on microhardness of glass-ionomer cements.
J Minim Interv Dent. 2008;1(1):66-76. http://mi-compendium.
org/journal/index.php/JMID/article/view/12/11 Accessed May 4, 2016.
26. Algera TJ, Kleverlaan CJ, de Gee AJ, Prahl-Andersen B, Feilzer AJ. The influence of accelerating the setting rate by ultra- sound or heat on the bond strength of glass ionomers used as orthodontic bracket cements. Eur J Orthod. 2005;27(5):472-476.
27. Daifalla LE, Mobarak EH. Effect of ultrasound application during setting on the mechanical properties of high viscous glass-ionomers used for ART restorations. J Adv Res. 2015;
6(6):805-810.
28. Wiegand A, Buchalla W, Attin T. Review on fluoride-releasing restorative materials—fluoride release and uptake character- istics, antibacterial activity and influence on caries formation.
Dent Mater. 2007;23(3):343-362.
29. Baig MS, Fleming GJ. Conventional glass-ionomer materials:
A review of the developments in glass powder, polyacid liq- uid and the strategies of reinforcement. J Dent. 2015;43(8):
897-912.
30. Sungurtekin-Ekci E, Ozdemir-Ozenen D, Duman S, Acuner IC, Sandalli N. Antibacterial surface properties of various fluoride- releasing restorative materials in vitro. J Appl Biomater Funct Mater. 2015;13(2):e169-e173.
31. Wilder AD, Boghosian AA, Bayne SC, Heymann HO, Sturdevant JR, Roberson TM. Effect of powder/liquid ratio on the clinical and laboratory performance of resin-modified glass-ionomers.
J Dent. 1998;26(4):369-377.